Influence of low-fracture-fiber mechanism on fiber/melt-flow behavior and tensile properties of ultra-long-glass-fiber-reinforced polypropylene composites injection molding
學年 109
學期 1
出版（發表）日期 2020-11-19
作品名稱 Influence of low-fracture-fiber mechanism on fiber/melt-flow behavior and tensile properties of ultra-long-glass-fiber-reinforced polypropylene composites injection molding
作品名稱（其他語言）
著者 Po-Wei Huang; Hsin-Shu Peng; Sheng-Jye Hwang; Chao-Tsai Huang
單位
出版者
著錄名稱、卷期、頁數 Journal of Polymer Engineering 41(2), p. 155-163
摘要 In this study, an injection molding machine with a low-fracture-fiber mechanism was designed with three stages: a plasticizing stage, an injection stage, and a packing stage. The fiber-fracture behavior is observed under the screw (plasticizing stage) of low-compression/shear ratio for the ultra-long fiber during the molding process. The molding material employed in this study was 25-mm-ultra-long-glass-fiber-reinforced polypropylene (PP/U-LGF). In addition, a thickness of 3 mm and a width of 12 mm spiral-flow-mold were constructed for studying the melt flow length and flow-length ratio through an experiment. The experimental results showed that the use of an injection molding machine with a three-stage mechanism decreased the fiber length when the screw speed was increased. On average, each fiber was shortened by 50% (>15 mm on average) from its original length of 25 mm. Longer glass fibers were more resistant to melt filling, and as the fiber length was reduced, the mixing between the melt and glass fibers was improved. Thus, the melt fluidity and fiber ratios were increased. In addition, the mixing/flow direction of the melt had an impact on the dispersion and arrangement of glass fibers, thus the tensile strength of PP/U-LGF increased.
關鍵字 fiber-fracture behavior;injection molding machine;melt flow length ratio;tensile strength;ultra-longglass-fiber-reinforced composites
語言 en
ISSN 0334-6447; 2191-0340
期刊性質 國外
收錄於 SCI
產學合作 國內
通訊作者 Hsin-Shu Peng
審稿制度 是
國別 DEU
公開徵稿
出版型式 ,電子版,紙本
相關連結

機構典藏連結 ( http://tkuir.lib.tku.edu.tw:8080/dspace/handle/987654321/120218 )

SDGS 可負擔的潔淨能源,尊嚴就業與經濟發展,產業創新與基礎設施,永續城市與社區,負責任的消費與生產