The Morphology and Control Release Behavior of Thermosensitive Poly(N-Isopropylacrylamide-Methylacrylic acid)/Au Semi-hollow Composite Latex Particles
學年 104
學期 2
發表日期 2016-07-25
作品名稱 The Morphology and Control Release Behavior of Thermosensitive Poly(N-Isopropylacrylamide-Methylacrylic acid)/Au Semi-hollow Composite Latex Particles
作品名稱（其他語言）
著者 Hsu, Mei-Ling; Don, Trong-Ming; Lee, Chia-Fen
作品所屬單位
出版者
會議名稱 The 32th International Conference of the Polymer Processing Society (PPS-32)
會議地點 Lyon, France
摘要 In this work, the poly(methyl methacrylate-co-methacrylic acid)/poly(methacrylic acid-co-N-isopropylacrylamide) thermosensitive composite semi-hollow latex particles were synthesized by three processes. The first process was to synthesize the poly(methyl methacrylate-co-methacrylic acid) (poly(MMA-MAA)) copolymer latex particles by the method of soapless emulsion polymerization. The second process was to polymerize methacrylic acid (MAA), N-isopropylacrylamide (NIPAAm) and crosslinking agent, N,N’-Methylenebisacrylamide (MBA), in the presence of poly(MMA-MAA) latex particles to form the linear poly(MMA-MAA)/crosslinking poly(MAA-NIPAAm) core-shell latex particles with solid structure. In the third process, part of the linear poly(MMA-MAA) core of core-shell latex particles was dissolved by ammonia to form the thermosensitive poly(MMA-MAA)/poly(MAA-NIPAAm) semi-hollow latex particles. The morphologies of the semi-hollow latex particles show that there is a hollow zone between the linear poly(MMA-MAA) core and the crosslinked poly(MAA-NIPAAm) shell. The crosslinking agent and shell composition significantly influenced the lower critical solution temperature (LCST) of poly(MMA-MAA)/poly(MAA-NIPAAm) semi-hollow latex particles. Besides, the gold nanoparticles (Au NP) were produced by the method of condensation, and wrapped in the thermosensitive poly(MMA-MAA)/poly(MAA-NIPAAm) semi-hollow latex particles to form the poly(MMA-MAA)/poly(MAA-NIPAAm)/Au semi-hollow composite latex particles, and then the composite latex particles were used as carriers to load with Arbutin. The morphologies and the behavior of control release of the composite latex particles were investigated.
關鍵字
語言 en
收錄於
會議性質 國際
校內研討會地點 無
研討會時間 20160725~20160729
通訊作者
國別 FRA
公開徵稿
出版型式
出處 The 32th International Conference of the Polymer Processing Society Proceeding
相關連結

機構典藏連結 ( http://tkuir.lib.tku.edu.tw:8080/dspace/handle/987654321/107553 )