Electrical Properties of Sm-doped Ceria (SDC) and SDC Carbonate Composite
學年 102
學期 1
出版（發表）日期 2013-11-01
作品名稱 Electrical Properties of Sm-doped Ceria (SDC) and SDC Carbonate Composite
作品名稱（其他語言）
著者 Wen, L.C.; Hsieh, C. Y.; Tsai, Y. I.; Lin, H. K.; Chang, S. C.; Kao, H.-C.I.; Sheu, H.S.; Lee, M.C.; Lee, Y.S.
單位 同步輻射中心核能研究所 淡江大學化學學系
出版者 Oxford: Wiley-Blackwell Publishing Ltd.
著錄名稱、卷期、頁數 Journal of the Chinese Chemical Society 60(11), pp.1359–1364
摘要 This study prepared a dense Sm-doped ceria (SDC) and an SDC carbonate composite (abbreviated as SDC-C). The latter was prepared by immersing porous SDC with a formula of (Ce0.8Sm0.2)O1.9 and a relative density of approximately 65-70% into a molten mixture of carbonates containing 1:1 molar ratio of Li2CO3 and Na2CO3 at 500 °C. The relative density of the SDC-C was close to 100%. In addition, SDC oxide without carbonates, which also has a relative density of close to 100%, was heat treated at 1600 °C. At 500 °C, the electrical conductivity and ionic transference number (ti) of the SDC oxide were 1.79(5) × 10−3 S·cm−1 and 0.99(2), respectively, such that electronic conduction could be disregarded. Increasing the temperature caused a gradual decrease in the ti of SDC. Following the addition of carbonates to SDC, the electrical conductivity reached 1.23(9) × 10−1 S·cm−1 at 500 °C. After 14 days (340 h), the electrical conductivity of the SDC-C at 490 °C, leveled off at about 6 × 10−2 S·cm−1. SDC-C could be used as a potential electrolyte in solid oxide fuel cells (SOFCs) at temperatures below 500 °C.
關鍵字 SDC; Carbonate; Composite; Relative ensity; Conductivity
語言 en_US
ISSN 2192-6549; 0009-4536
期刊性質
收錄於 SCI
產學合作 國內
通訊作者 高惠春
審稿制度 是
國別 GBR
公開徵稿
出版型式 電子版
相關連結

機構典藏連結 ( http://tkuir.lib.tku.edu.tw:8080/dspace/handle/987654321/92956 )

機構典藏連結