作品名稱 Concrete reinforced with up to 0.2 vol% of short carbon fibres
作品名稱（其他語言）
著者 Chen, Pu-woei; Chung, D.D.L
單位 淡江大學航空太空工程學系暨研究所
出版者 Kidlington: Pergamon
著錄名稱、卷期、頁數 Composites 24(1), pp.33-52
摘要 The use of short pitch-based carbon fibres (0.5% by weight of cement, 0.189 volume % (vol%) of concrete), together with a dispersant, chemical agents and silica fume, in concrete with fine and coarse aggregates resulted in a flexural strength increase of 85%, a flexural toughness increase of 205%, a compressive strength increase of 22%, and a material price increase of 39%. The slump was 102 mm (4 in) at the optimum water/cement ratio of 0.50. The air content was 6%, so the freeze-thaw durability was increased, even in the absence of an air entrainer. The aggregate size had little effect on the above properties. The minimum carbon fibre content for flexural strength increase was 0.1 vol%, although the flexural toughness was still increased below this fibre volume fraction. The optimum fibre length was such that the mean fibre length decreased from 12 mm before mixing to 7 mm after mixing, which used a Hobart mixer. The drying shrinkage was decreased by up to 90%. The electrical resistivity was decreased by up to 83%.
關鍵字 composite materials; fibre-reinforced concrete;mechanical properties;mix formulation;aggregate size;air content;fibre volume fraction;short carbon fibres
語言 en
ISSN 1359-8368
期刊性質 國外
收錄於
產學合作
通訊作者 Chen, P-W; Chung, DDL
審稿制度 否
國別 GBR
公開徵稿
出版型式 ,紙本
相關連結

機構典藏連結 ( http://tkuir.lib.tku.edu.tw:8080/dspace/handle/987654321/62367 )

機構典藏連結
SDGS 優質教育,產業創新與基礎設施