教師資料查詢 | 類別: 期刊論文 | 教師: 高惠春KAO, HUEY-CHUEN (瀏覽個人網頁)

標題:Preparation of compact Li-doped Y2Ti2O7 solid electrolyte
學年100
學期1
出版(發表)日期2012/01/01
作品名稱Preparation of compact Li-doped Y2Ti2O7 solid electrolyte
作品名稱(其他語言)
著者Wen, L.C.; Hsieh, H.Y.; Lee, Y.H.; Chang, S.C.; Kao, H.-C.I.; Sheu, H.S.; Lin, I.N.; Chang, J.C.; Lee, M.C.; Lee, Y.S.
單位淡江大學化學學系
出版者Amsterdam: Elsevier BV * North-Holland
著錄名稱、卷期、頁數Solid State Ionics 206, pp.39–44
摘要Three series of solid electrolytes were prepared with the nominal compositions of (Y2−xLi3x)Ti2O7 (Y3LT), (Y2−xLix)Ti2O7−x(YLT)and Y2−xTi2O7−3x/2 (YT) with x = 0.040 − 0.11. Comparing the unit cell a-axis of the YLT with that of YT, the latter is shorter with the same amount of x. This indicates a successful substitution of the Li ion into the Y site of Y2Ti2O7. However, both Y3LT and YLT have exactly the same unit cell a-axis length with the same amount of x so that the solid solution formed probably has the same formula, (Y2−xLix)Ti2O7−x, in which only one Li ion is substituted into the Y site. Extra Li2O added in the Y3LT is probably acting as a self flux to lower the melting point of the mixture. As a result, materials become more compact and grains grow bigger. One compound of Y3LT with x = 0.060 has a total conductivity of 4.3(4) × 10− 4 S⋅cm− 1 at 700 °C. Adding Li2O as a flux and carefully controlling the heat treatment history, compact sample of Y3LT with a relative density higher than 90% was obtained at a temperature as low as 1150 °C. Its ionic conductivity is comparable to one Y2Ti2O7 prepared at 1600 °C with a conductivity reported as 2.30 × 10− 4 S⋅cm− 1.
關鍵字(Y2 − xLix)Ti2O7 − x;Pyrochlore;Titanate;Li2O;Oxygen ion conductor
語言英文
ISSN0167-2738
期刊性質國外
收錄於SCI;
產學合作國內;
通訊作者高惠春
審稿制度
國別荷蘭
公開徵稿
出版型式,電子版,紙本
相關連結
SDGs
Google+ 推薦功能,讓全世界都能看到您的推薦!