Unusual mechanical properties of melt-blended poly(lactic acid) (PLA)/clay nanocomposites
學年 102
學期 2
出版(發表)日期 2014-03-01
作品名稱 Unusual mechanical properties of melt-blended poly(lactic acid) (PLA)/clay nanocomposites
作品名稱(其他語言)
著者 Lai, Sun-Mou; Wu,Sheng-Huang; Lin, Gwo-Geng; Don, Trong-Ming
單位 淡江大學化學工程與材料工程學系
出版者 Kidlington: Pergamon
著錄名稱、卷期、頁數 European Polymer Journal 52, pp.193–206
摘要 The commercial organic-modified clay was incorporated into a nearly amorphous PLA matrix using a melt-blending process to form PLA/clay nanocomposites. The nanocomposite containing 1 phr of clay conferred the highest exfoliation of clay among all investigated clay dosages. Especially, only this particular nanocomposite had a lower modulus and exhibited significant stress-whitening and necking behavior with a large extension, elongation at break being increased to 208%, up to 37-fold increment compared to the neat PLA. Based on SEM and TEM pictures, the highly exfoliated platelets produced a relatively large interfacial area between the clay platelet and PLA matrix, which resulted in a comprehensively plasticized interfacial region. The highly plasticized interfacial region and the well-dispersed clay platelets with high aspect ratio, particular for thin samples, enhanced the multiple shear-banding which induced the plastic deformation and substantial shear yielding behavior. It also caused a decrease in the spherulite nucleation behavior of the PLA. On the contrary, when the clay was added at higher amounts, it existed mostly in the form of intercalated structure which acted as rigid filler, raising the modulus and causing an early failure in the tensile test. Both Halpin–Tsai and Mori–Tanaka equations were used to predict the modulus of the nanocomposites at higher clay contents where the Mori–Tanaka equation gave a better prediction.
關鍵字 Poly(lactic acid);Clay;Nanocomposites;Mechanical properties;Exfoliation
語言 en
ISSN 0014-3057
期刊性質 國外
收錄於 SCI EI
產學合作
通訊作者 Don, Trong-Ming
審稿制度
國別 GBR
公開徵稿
出版型式 ,電子版,紙本
相關連結

機構典藏連結 ( http://tkuir.lib.tku.edu.tw:8080/dspace/handle/987654321/96888 )

機構典藏連結