High Temperature Interfacial Reaction between Glass Gobs and Sol-Gel Coated Al2O3 Films
學年 98
學期 1
出版（發表）日期 2009-09-01
作品名稱 High Temperature Interfacial Reaction between Glass Gobs and Sol-Gel Coated Al2O3 Films
作品名稱（其他語言）
著者 Chien, Hsi-hsin; Ma, Kung-jeng; SV Prabhakar Vattikuti; Kuo, Chien Hung; Huo, Zen Bong; Chao, Choung-lii
單位 淡江大學機械與機電工程學系
出版者 Stafa-Zurich: Trans tech publications
著錄名稱、卷期、頁數 Advanced Materials Research76-78, pp.708-712
摘要 Glass molding process is considered to have a great potential for the mass production of optical components with lower cost. Up to now, the service life of molding dies is still not satisfied. This study mainly focuses on the development of sol-gel derived Al2O3 coatings in order to extend the service life of glass molding dies. High temperature glass wetting experiment was carried out to investigate the high temperature interfacial reaction between the coatings and glass gobs. The 304 stainless steel were used as the substrate materials. The sol-gel coated Al2O3 was selected as the protective coating. OHARA L-BAL42 glass gobs were chosen as the test materials. It can be observed that very severe interfacial reaction occurs between stainless steel and glass at high temperature. The contact angle dramatically decreases from initial and then gradually approaches 25° at 825℃ after 2 minutes holding time. The severe interface chemical reaction also results in the loss of transparency in glass appearance. The reaction products such as Zn and Ba are mainly from glass material. For the case of Al2O3 coated substrate, the variation of the contact angles varied from 152 to 138°, presents anti-sticking or non wetting behavior. There are no reaction products can be found on the glass contacted area after wetting test.
關鍵字 Glass Molding;Interfacial Reaction;Sol-Gel Al2O3 Coating
語言 en
ISSN 1022-6680
期刊性質 國外
收錄於 EI
產學合作
通訊作者 Chien, Hsi-hsin
審稿制度
國別 CHE
公開徵稿
出版型式 紙本
相關連結

機構典藏連結 ( http://tkuir.lib.tku.edu.tw:8080/dspace/handle/987654321/65317 )

機構典藏連結
SDGS 產業創新與基礎設施