Microstructural and Mechanical Effects of Latex, Methylcellulose, and Silica Fume on Carbon Fiber Reinforced Cement
學年 85
學期 2
出版（發表）日期 1997-03-01
作品名稱 Microstructural and Mechanical Effects of Latex, Methylcellulose, and Silica Fume on Carbon Fiber Reinforced Cement
作品名稱（其他語言）
著者 Chen, Pu-woei; Fu, Xuli; Chung, D. D. L.
單位 淡江大學航空太空工程學系
出版者 Farmington Hills: American Concrete Institute
著錄名稱、卷期、頁數 ACI Materials Journal 94(2), pp.147-155
摘要 The effect of methylcellulose, silica fume, and latex on the degree of dispersion of short carbon fibers in cement paste (with water-reducing agent in an amount varying from 0 to 3 percent by weight of cement) was assessed. This degree, as indicated by the ratio of the measured volume of electrical conductivity to the calculated value, and the effectiveness of the fibers in enhancing the tensile/flexural properties attained by using methylcellulose and silica fume were higher than those attained by using methylcellulose alone or latex. Methylcellulose was superior to latex in giving a high degree of fiber dispersion at fiber volume fractions 1 percent, as measured by this technique, but latex resulted in superior tensile-flexural properties and lower content and size of air voids than methylcellulose. With the fiber content fixed at 0.53 vol. percent, the degree of fiber dispersion, as measured by this technique, decreased with increasing latex-cement ratio from 0.05 to 0.30, while the void content attained a minimum at an intermediate latex-cement ratio of 0.15. As a result of the former, the flexural toughness decreased monotonically with increasing latex-cement ratio. As a result of the latter, the flexural strength attained a maximum at an intermediate latex-cement ratio of 0.15. In contrast, both flexural toughness and strength increased monotonically with increasing latex-cement ratio when fibers were absent.
關鍵字 carbon;cements;concrete;flexural strength;latex (plastic);silica fume;voids
語言 en
ISSN 0889-325X
期刊性質 國外
收錄於 SCI EI
產學合作
通訊作者
審稿制度
國別 USA
公開徵稿
出版型式 紙本
相關連結

機構典藏連結 ( http://tkuir.lib.tku.edu.tw:8080/dspace/handle/987654321/45995 )

機構典藏連結
SDGS 優質教育,產業創新與基礎設施