作品名稱 | Performance properties of self-curing aqueous-based PU system with tri-glycidyl phosphate curing agent |
作品名稱(其他語言) | |
著者 | Wang, Shih-Chieh; Chen, Po-Cheng; Hwang, Jing-Zhong; Yeh, Jen-Taut; Huang, Chi-Yuan; Chen, Kan-Nan |
單位 | 淡江大學化學學系 |
出版者 | Dordrecht: Springer Netherlands |
著錄名稱、卷期、頁數 | Journal of Polymer Research 19(3), 9844(10pages) |
摘要 | Amino-terminated and carboxylic acid containing aqueous-based polyurethane (PU) dispersion was prepared by a conventional NCO-terminated PU prepolymer process by using isophorone diisocyanate (IPDI), polypropylene glycol-2000 (PPG-2000) and 2,2′-dimethylolpropanoic acid (DMPA) as the key raw materials. A new curing agent, tri-glycidyl phosphate (POG) was prepared from a substitution reaction of phosphorus oxychloride and glycidol. A single-component self-curable aqueous-based PU system is obtained from an addition of POG into aqueous-base PU dispersion and its curing reaction occurred among POG oxiranes and PU amino groups immediately after hydrophobic POG diffused into PU particles (as polymeric micelles). The cross-linked PU resins were resulted on drying at ambient temperature. Original PU dissolved into THF and ethanol. And its gel content increased to 90.1% and sample loss in ethanol decreased to 9.2% of this self-cured PU system with 5.0 phr POG. The limiting oxygen index (LOI) value is 20 of original PU and its LOI reached to 27 of this same self-cured PU system. The improved mechanical and thermal properties of those self-cured PU resins were evaluated, respectively in this report. |
關鍵字 | Self-curing; Aqueous-based PU; Glycidyl phosphate; Polymeric micelle |
語言 | en |
ISSN | 1022-9760; 1572-8935 |
期刊性質 | 國外 |
收錄於 | SCI |
產學合作 | |
通訊作者 | Chen, Kan-Nan |
審稿制度 | |
國別 | NLD |
公開徵稿 | |
出版型式 | 紙本 |
相關連結 |
機構典藏連結 ( http://tkuir.lib.tku.edu.tw:8080/dspace/handle/987654321/77002 ) |