Preparation and Superconductivity of a Series of Bi2CaSr(subscript (2-x))Ba(subscript x)Cu2O(subscript (8+δ))
學年 77
學期 2
出版(發表)日期 1989-06-01
作品名稱 Preparation and Superconductivity of a Series of Bi2CaSr(subscript (2-x))Ba(subscript x)Cu2O(subscript (8+δ))
作品名稱(其他語言) Preparation and superconductivity of a series of Bi2CaSr2-xBaxCu2O8+x
著者 王年豪; Wang, Nein-hour; 高惠春; Kao, Huey-chuen I.
單位 淡江大學化學學系
出版者 臺北市:中國化學學會
著錄名稱、卷期、頁數 Journal of the Chinese Chemical Society=中國化學會會誌 36(3), pp.205-210
摘要 By means of the addition of Ba into the Bi-Ca-Sr-Cu-O 2122 system, a series of Bi/sub 2/CaSr/sub 2-x/Ba/sub x/Cu/sub 2/O/sub 8+.delta./(0.ltoreq.x.ltoreq.2) quinary metal oxides were prepared by the citrate route and by the conventional powder reaction method. The samples prepared by the former method have better properties than the latter. It was found that.delta. was not equal to zero for all of them and that it increased with decreasing Tc. Two phases were identified in the oxides containing all five metal elements. One is the Bi-Ca-Sr-Cu-O 2122 phase, the other is a new insulating phase which probably contains Bi-Ca-Ba-Cu-O with undetermined stoichiometry. Superconductivity was found in those samples for which x.ltoreq.1.50 with their Tc onsets between 93-78 K by resistivity measurements. Superconductivity decreased monotonically with increasing x. However, residual resistance was found in those samples for which 1.00.ltoreq.x.ltoreq.1.50. The Meissner effect appears in the samples where x.ltoreq.1.00 with Tc onsets between 88-80 K. For x=1.75 and 2.00, the samples were semiconductors with resistivities of 6.66*10/sup 2/ and 6.96*10/sup 3/.OMEGA..bcdot.cm at 290K, and activation energies of 0.109, and 0.298eV, respectively.
關鍵字
語言 en
ISSN 0009-4536
期刊性質 國內
收錄於
產學合作
通訊作者
審稿制度
國別 TWN
公開徵稿
出版型式 ,紙本
相關連結

機構典藏連結 ( http://tkuir.lib.tku.edu.tw:8080/dspace/handle/987654321/25138 )

機構典藏連結