| 作品名稱 | Preparation of HMDS-modified silica/polyacrylate hydrophobic hard coatings on PMMA substrates |
| 作品名稱（其他語言） | |
| 著者 | Chang, Chao-ching; Wu, Yu-ting; Cheng, Liao-ping |
| 單位 | |
| 出版者 | |
| 著錄名稱、卷期、頁數 | Journal of Coatings Technology and Research 13(6), p.999-1007 |
| 摘要 | Colloidal silica nanoparticles synthesized from tetraethoxysiliane via a sol–gel process were surface modified by 3-(trimethoxysilyl)propyl methacrylate (MSMA) and 1,1,1,3,3,3-hexamethyldisilazane (HMDS). MSMA acted both as a C=C provider and a coupling agent, whereas HMDS was used to prevent particle aggregation and engender hydrophobicity. The modified silica particles (HMSiO2) were UV-cured together with the crosslinking agent, dipentaerythritol hexa-acrylate (DPHA) to form coatings on poly(methyl methacrylate) (PMMA) substrates. Dynamic light scattering of the synthesized sols indicated that the average size of HMSiO2 was ca. 10 nm, consistent with that obtained from TEM imaging. FTIR spectroscopic analyses demonstrated chemical attachment of HMDS to the silica particles. The cured coatings were characterized in terms of water contact angle, light transmittance, hardness, abrasion resistance, and surface morphology. It was found that hydrophobicity of the coatings increased while light transmittance and hardness decreased with increasing HMDS content. DPHA played the role of providing mechanical strength and adherence; however, the coatings became lightly hazy when the weight ratio of DPHA/silica fell in the range 0.3–0.7. In the optimal case, a hard coating (4H) with water contact angle of 108 and transmittance of 100% (vs PMMA) had been obtained at the DPHA content of 10 wt%. |
| 關鍵字 | Silica nanoparticle;Hard coating;Transparent;Hydrophobicity;Nanocomposite coating |
| 語言 | en_US |
| ISSN | 1547-0091;1935-3804 |
| 期刊性質 | 國外 |
| 收錄於 | SCI TSSCI EI |
| 產學合作 | |
| 通訊作者 | Cheng, Liao-ping |
| 審稿制度 | 是 |
| 國別 | USA |
| 公開徵稿 | |
| 出版型式 | ,電子版,紙本 |
| 相關連結 |
機構典藏連結 ( http://tkuir.lib.tku.edu.tw:8080/dspace/handle/987654321/108861 ) |