| 作品名稱 | Effects of high energy Au-ion irradiation on the microstructure of diamond films |
| 作品名稱（其他語言） | |
| 著者 | Chen, Shih-Show; Chen, Huang-Chin; Wang, Wei-Cheng; Lee, Chi-Young; Lin, I-Nan; Guo, Jinghua; Chang, Ching-Lin |
| 單位 | 淡江大學物理學系 |
| 出版者 | College Park: American Institute of Physics |
| 著錄名稱、卷期、頁數 | Journal of Applied Physics 113(11), 113704(10pages) |
| 摘要 | The effects of 2.245 GeV Au-ion irradiation and subsequent annealing processes on the evolution of microstructure of diamond films with microcrystalline (MCD) or ultra-nanocrystalline (UNCD) granular structure were investigated, using near edge x-ray absorption fine structure and electron energy loss spectroscopy in transmission electron microscopy. For MCD films, the Au-ion irradiation disintegrated some of the diamond grains, resulting in the formation of nano-sized carbon clusters embedded in a matrix of amorphous carbon (a-C). The annealing process recrystallized the diamond grains and converted the a-C into nano-sized graphite particulates and, at the same time, induced the formation of nano-sized i-carbon clusters, the bcc structured carbon with a0 = 0.432 nm. In contrast, for UNCD films, the Au-ion irradiation transformed the grain boundary phase into nano-sized graphite, but insignificantly altered the crystallinity of the grains of the UNCD films. The annealing process recrystallized the materials. In some of the regions, the residual a-C phases were transformed into nano-sized graphites, whereas in other regions i-carbon nanoclusters were formed. The difference in irradiation-induced microstructural transformation behavior between the MCD and the UNCD films is ascribed to the different granular structures of the two types of films. |
| 關鍵字 | |
| 語言 | en_US |
| ISSN | 0021-8979 1089-7550 |
| 期刊性質 | 國外 |
| 收錄於 | |
| 產學合作 | |
| 通訊作者 | |
| 審稿制度 | |
| 國別 | USA |
| 公開徵稿 | |
| 出版型式 | 紙本 電子版 |
| 相關連結 |
機構典藏連結 ( http://tkuir.lib.tku.edu.tw:8080/dspace/handle/987654321/93421 ) |